ASTM E340 PDF

Macroetching, also known as deep etching, involves etching specimens prepared with a suitable acid or reagent for macrostructural examination. Contact us. 1 This test method is under the jurisdiction of ASTM Committee E-4 on. Metallography and is the direct responsibility of Subcommittee E on Sam- pling. 10 Nov ASTM E Standard Test Method for Macroetching Metals and Alloys_ 机械/仪表_工程科技_专业资料。美国材料与试验协会(ASTM)标准.

Author: Kim Vudolmaran
Country: Solomon Islands
Language: English (Spanish)
Genre: Business
Published (Last): 12 December 2013
Pages: 97
PDF File Size: 5.76 Mb
ePub File Size: 2.68 Mb
ISBN: 290-3-26629-219-3
Downloads: 83011
Price: Free* [*Free Regsitration Required]
Uploader: Voshakar

Evaluation of heat treated parts to determine locations of hard or soft spots, tong marks, quench cracks, case depth in induction hardened or carburized parts, and effectiveness of stop-off coatings.

The most common reagent for macroetching iron and steel is a 1: Go to Navigation Go to Content. The copper industry uses macroetching for control of surface porosity in wire bar.

ASTM E Standard Test Method for Macroetching Metals and Alloys_百度文库

Aztm specimens and chemical analyses will provide the necessary detailed information about specific localities but they cannot give data about variation from one place to another unless an inordinate number of specimens are taken.

In the aluminum industry, macroetching is used to evaluate extrusions as well as the other products such as forgings, sheets, and so forth.

Macroetching will also show the presence of asm and voids, such as seams, laps, porosity, flakes, bursts, extrusion rupture, cracks, and so forth. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. Historical Version s – view previous versions of astn Translated Version s: Forge shops, in addition, use macroetching to reveal flow lines in setting up the best forging practice, die design, and metal flow.

Macroetch Examinations

In the machine shop, it can be used for the determination of grinding cracks in tools and dies. Chemical analyses e3340 other means of determining the chemical composition would have to be performed to determine the extent of variation. Historical Version s – view previous versions of standard.

The information provided about variations in chemical composition is strictly qualitative but the location of extremes in segregation will be shown. Click here to request a quote Chicago Lab: Forging shops and foundries also use macroetching to determine the presence of internal faults and surface defects.

Macroetching, also known as deep etching, involves etching specimens prepared with a asttm acid or reagent for macrostructural examination ast, low magnifications and rating by a grades series of photographs showing the incidence of certain conditions such as: Other applications of macroetching include: Macroetch Examinations Macroetching, also known as deep etching, involves etching specimens prepared with a suitable acid or reagent for macrostructural examination at low magnifications and rating by a grades series of photographs showing the incidence of certain conditions such as: Link to Active This link will always route to the current Active version of the standard.

The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

Click here to request a quote. For specific warning statements, see 6. Development of grain flow in a forged part or fastener, which is a critical property for the integrity of the forging.

It is the responsibility of the user of this standard to asfm appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Evaluation of machined parts for grinding cracks in tools and dies. Defects such as coring, cracks, and porthole die welds are identified.

ASTM E – 15 Standard Practice for Macroetching Metals and Alloys

For an example of the use of macroetching in the steel forging industry see Method E It is also used in the heat-treating shop to determine location of hard or soft spots, tong marks, quenching cracks, case depth in shallow-hardening steels, case depth in carburization of dies, effectiveness of d340 coatings in carburization, and so forth.

Contact our sales team to assist in specification review or a cost estimate for your testing. Study of weld structures, definition of weld penetration, dilution of filler metal by base metals, entrapment of flux, porosity, and cracks in weld and heat affect zones, etc. The metallurgical engineering team at SGS MSi has the expertise to meet all your material requirements for acid etch processes.